Charpy impact strength

5,62 kJ / m2

Tensile strength along layers

34,8 MPa

Tensile modulus along layers

1,32 GPa

Flexural strength

94,2 MPa

Flexural modulus

3,04 GPa

Maximum bending load

154 n

Tensile strength across layers

31,2 MPa

Tensile modulus across layers

3,07 GPa

Maximum tensile load

1419 n

Compressive strength

77,4 MPa

Compressive modulus

2,96 GPa

Maximum compressive load

9719 n

Elongation ratio

30%

Biodegradability

Yes

The dielectric constant

3,95x1013 OM / cm

Yield strength at stretching and at a temperature of 23 ° C

n / a

Flexural strength 2,8 mm / min. 23 ° C

n / a

Rockwell hardness (R scale) Impact

n / a

Oil and petrol resistance (maximum shape change in 24 hours)

0,3%

Oxygen index,% O2 according to GOST 21793-76

20.8-21.0%

Ash content according to GOST 15973

Less than 0,01%

Melting temperature

173-178 °C (７７°F)

softening temperature

50°C

Hardness (Rockwell)

R70-R90

Elongation at break

3,8%

Flexural strength

55,3 MPa

Tensile strength

57,8 MPa

Tensile modulus

3,3 GPa

Flexural modulus

2,3 GPa

Glass transition temperature

60-65 °C (７７°F)

Density

1,23-1,25 g / cm³